Over the past decade, many countries have heavily invested in wind energy. While the quality control, routine inspection, and performance monitoring of the turbine and the blades have significantly developed over the past few years, the quality control and monitoring of the foundation elements is often overlooked. This is essential in keeping these massive towers grounded and secure.
Wind Turbine foundation can be as large as 10-15 meters (diameter), the Foundation block can be as thick as 1 to 2 meters, depending on the tower size, and soil characteristics. Due to their relatively large size, these foundations are often considered mass concrete.
This can lead into buildup of significant heat (from the cement hydration process) and develop massive temperature gradient in the foundation block. This may result in thermal contraction cracking shortly after the concrete hardens — compromising the structural integrity and durability of the foundation.
Excessive heat development and dissipation may result in thermal contraction cracking shortly after the concrete hardens — compromising the structural integrity and durability of the foundation.
Wind Turbine Foundations have sophisticated congested steel reinforcement to provide stability against dynamic loads. This will make the placement of concrete challenging, and it may result in poor quality patches in the foundation.
While the use of Self-Consolidating Concrete (SCC) and steel fibres can help overcome some of these challenges, by reducing the amount of steel bars, and proper placement. However, the quality of foundations needs to be evaluated ahead of installing the tower and the turbine.
Quality Control of Wind Turbine Foundation
Routine quality control tests such as slump test (flow test in case of SCC), air content, and strength measurement are necessary to monitor the strength development in concrete mass foundations. The process of concrete placement and curing should be carefully planned.
Any interruptions in work, or change in work order should be fully recorded. After placement, proper curing regime should be adopted to eliminate the risk of early age shrinkage cracking.
Another issue could be alkali-silica reactions. Since these foundations are normally exposed, the risk of ASR will be high should the aggregates are potentially reactive.
Non-Destructive Testing can be used to evaluate the quality of these foundations during and after hardening.
1- Temperature and Strength Monitoring
Monitoring temperature gradient in mass concrete is important in minimizing the risk of cracking after hardening. Temperature sensors (wired and wireless) can be used to collect information from different locations of the foundations. Moreover, depending on the type of concrete, this information can be translated into concrete strength using maturity method.
Maturity method provides a simple approach for evaluating the strength of cement-based materials in real-time, i.e. during construction .
2- Ultrasonic Tomography
Ultrasonic Tomography can be used to evaluate the shallow depth deficiencies in the foundations. Depending on reinforcement pattern, this technique provides a reliable and cost-effective tool to scan concrete for potential defects. The method works based on transmitting and receiving ultrasonic signal from an array of transducers; the collected signals are merged to develop 2D maps of sub-surface defects, or other anomalies.
Impact-Echo is a nondestructive test method for evaluating concrete and masonry structures. The test utilizes stress waves (sound) that is normally generated through striking concrete by an impactor (Impact), and recording the reflections and refraction from internal flaws and other boundaries (Echo).
As P- and S- waves propagate within concrete element, they get reflected by internal interfaces (concrete-crack, concrete-air, concrete-rebar) or external boundaries. The arrival of these echos on the surface induces displacement. This displacement can be measured by placing a sensitive transducer (which then converts displacement or acceleration into electrical voltage). Data is recorded by a data acquisition and data logging system. Learn More about Impact-Echo
The method can be used to identify delamination, discontinuity and major voids within the foundation blocks. In foundations with known thickness, the results can be analyzed to show the depth of defects.
4- Ground Penetrating Radar
Ground penetrating radar (GPR) is a very useful technique for nondestructive concrete imaging and scanning. GPR uses pulsed electromagnetic radiation to scan concrete. GPR consists of a transmitter antenna and a receiver antenna, and a signal processing unit. GPR emits electromagnetic pulses (radar pulses) with specific central frequency to scan the subsurface medium. The reflected waves from subsurface layers, and objects are captured by the receiver antenna.
Cracks in Wind Turbine Foundation
It is critical to repair early age cracks in wind turbine foundations. Wind turbine structures are subject to dynamic loads from the oscillation of tower, blades, and the operation of turbine. Due to this changing load, the cracks can progress in width, and depth, creating durability related issues and structural performance concerns. epoxy injecting into these cracks can help control these cracks at the early stage.